Fiberthree F3 PA Pure Lite Natural | 1.75mm | 200g
- Reviews (0)
Technical filament from polyamide modified for 3D-printing in FFF.
- Filament for FFF-printers with major PA 12 content
- high tensile strength; very low water absorption
- low warping effect
- excellent adhesion to various print plates
- very smooth surfaces possible (bone white color)
Material shows excellent strength with excellent impact resistance and reduced warping behaviour.
Recommended for all high strength parts with good heat- and media resistance.
The material can be used as a baseline for comparison of the fiber addition impact or where fibers or conductivity is not wanted in the printed part.
The material differs from PA PurePro by increased heat absorption in the melting process and a decreased moisture sensitivity.
Printed parts show an excellent smooth surface finish.
|Modulus of Elasticity printed specimen||MPa (N/mm²)||3.300|
|Tensile strength printed specimen x-y (+ 45°/-45°)||MPa (N/mm²)||60|
|Tensile strength printed specimen x-y (0°)||MPa (N/mm²)||80|
|Tensile strength printed specimen x-y (90°)||MPa (N/mm²)||30|
|Tensile stress printed specimen x-y (0°)||MPa (N/mm²)||—|
|Elongation printed specimen (0°)||%||—|
|Flexural modulus printed specimen (+ 45°/-45°)||GPa (kN/mm²)||—|
|Impact strength printed specimen x-y (+ 45°/-45°)(Charpy)||kJ/m²||135|
|Glass transition temp.||°C||88|
|Heat distortion temp.(HDT)||°C||90|
The Material has been tested on following printers:
|Printer||F3 PA-CF Pro||F3 PA-GF Pro||F3 PA Pure Pro||F3 PA-CF Lite||F3 PA Pure Pro|
|Evo-Tech Evolizer EL-102||x||x||x||x||x|
|Prusa I3 MK3S||x||x||x|
|Raise3D N2/N2+ (Bondtech-upgrade)||x||x||x||x||x|
|Zortrax M200 Plus||x||x|
Be the first to review “Fiberthree F3 PA Pure Lite Natural | 1.75mm | 200g”
You must be logged in to post a review.
There are no reviews yet.