Fiberthree F3 PA Pure Pro Black | 1.75mm | 2kg

Description

Technical filament from polyamide modified for 3D-printing in FFF.

• Filament for FFF-printers with major PA 6 content
• unfilled
• high tensile strength; moderate water absorption
• low warping effect
• excellent adhesion to various print plates

Material Properties

Material shows nearly similar strength for injection-molded or printed parts by the good layer adhesion with highly reduced warping behaviour.

Recommended for all high strength parts with good heat- and media resistance.

The material can be used as a baseline for comparison of the fiber addition impact or where fibers or conductivity is not wanted in the printed part.

The material differs from PA PureLite by less heat absorption in the melting process and a lightly increased moisture sensitivity.

Technical Information

Mechanical properties

Density	g/ cm³	1,2
Modulus of Elasticity printed specimen	MPa (N/mm²)	3400
Tensile strength printed specimen x-y (+ 45°/-45°)	MPa (N/mm²)	80
Tensile strength printed specimen x-y (0°)	MPa (N/mm²)	80
Tensile strength printed specimen x-y (90°)	MPa (N/mm²)	30
Tensile stress printed specimen x-y (0°)	MPa (N/mm²)	77,31
Elongation printed specimen (0°)	%	3,56
Flexural modulus printed specimen (+ 45°/-45°)	GPa (kN/mm²)	2,37
Impact strength printed specimen x-y (+ 45°/-45°)(Charpy)	kJ/m²	—
Shore hardness	—	—

Thermal properties

Glass transition temp.	°C	72
Heat distortion temp.(HDT)	°C	90

Data Sheets

Download Technical Data Sheet

Download Safety Data Sheet

Printers

The Material has been tested on following printers:

Printer	F3 PA-CF Pro	F3 PA-GF Pro	F3 PA Pure Pro	F3 PA-CF Lite	F3 PA Pure Pro
3NTR A2/A4	x	x	x	x	x
Evo-Tech Evolizer EL-102	x	x	x	x	x
Hage3D 84L/140L	x	x	x	x	x
Multec M500/M800	x	x	x	x	x
Prusa I3 MK3S	x	x	x
Raise3D N2/N2+ (Bondtech-upgrade)	x	x	x	x	x
Raise3D Pro2/Pro2+	x	x	x
UltiMaker S5/S3	x	x	x	x	x
Zortrax M200 Plus		x	x