Kimya ABS Carbon Black | 500g

Kimya ABS Carbon Black | 500g

£51.84 inc. VAT

£43.20 ex. VAT

The 3D filament Kimya ABS Carbon belongs to the styrenic polymer family. Acrylonitrile-butadiene-styrene-carbon (ABS Carbon) is a mixture of ABS and carbon fibers. ABS Carbon improves inter-layer adhesion and the compression resistance of the printed part.

Clear

Description

The 3D filament Kimya ABS Carbon belongs to the styrenic polymer family. Acrylonitrile-butadiene-styrene-carbon (ABS Carbon) is a mixture of ABS and carbon fibers. ABS Carbon improves inter-layer adhesion and the compression resistance of the printed part. Parts that are 3D printed using this filament are lighter and less fragile than when using standard ABS. It is used to produce frames, supports, shells and propellers. It is also highly valued by manufacturers of drones and by modeling aficionados. The Kimya ABS Carbon 3D filament has the following properties:

  • No shrinkage
  • Better tensile modulus than ABS
  • Better interplayer adhesion
  • Light weight objects

Technical Information

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.032 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@220°C – 10 kg) 35.7 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min – 20-220°C) 100 °C
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – 20-220°C) 30 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 50 mm/s
Infill 100% – rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 260°C
Bed T° 100°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES
Tensile modulus ISO 527-2/5A/50 2,189 MPa
Tensile Strength ISO 527-2/5A/50 37.4 MPa
Tensile Stress at Break ISO 527-2/5A/50 33.2 MPa
Tensile strain at break ISO 527 3 %
Flexural modulus ISO 178 1,822 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 56.6 MPa
Charpy impact resistance ISO 179-1/1eA 7 kJ/m²
Shore Hardness ISO 868 93D

Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.

Note 2 The data should be considered as indicative values – Properties can be influenced by production conditions.

Print Setting

Print speed: 50 mm/s

  • Extrusion temperature: 260°C
  • Platform temperature: 100°

 

Data Sheets

 Download Technical Data Sheet

 Download Safety Data Sheet

Miscellaneous

Spool Material PC
Steaming Temperature 120°C
Steaming Duration 4h-6h